- C-MB10L, called Liquid Silicon, In the process of cement hydration, the gel can be formed by reaction with calcium hydroxide, and the volume expansion can be produced in the solidification process of cement slurry, which can promote the development of cement strength in the process of cement curing, greatly reduce the permeability of cement paste, and thus improve the gas resistance of cement paste.
Application
- Temperature：≤180℃(BHCT)
- Addition：Recommend addition 6%
Physics & Chemic Index
| Item | Index |
| Granule Size>45μm% | ≤0.1 |
| PH | 6.0-9.0 |
| Density，g/cm3 | 1.30-1.40 |
| Apparent viscositym Pa.s | ≤40 |
| Solid content，% | 47.0-50.0 |
| Freezing point℃（winter） | ≤-10 |
- C-MB10L,using280kggalvanized bucket, or according to customers’ requirement.
- Ventilated, cool, dry condition, avoid of shining and raining. Guarantee period in 6months